柏延平¹  ,  夏    懿¹  ,  马    雷¹  ,  雒亿平²

 

( 1 .  国网甘肃省电力公司临夏供电公司 ，临夏 731100 ;

2.  西安理工大学 西北旱区生态水利国家重点实验室 ，西安 710048)

摘   要 ：研究旨在开发粉煤灰基地聚物固化剂替代水泥用于黄土加固 ， 以粉煤灰为主要前驱体 ，偏高岭土为铝质校正料 ，硅酸钠与氢氧化钠复合配制碱激发剂 ，通过正交试验考察碱激发剂模数 、固体掺量及粉煤灰掺量对抗压强度的影响。结果表明：最优配比为碱激发剂模数 1 . 1 、固体掺量 7% 、粉煤灰掺量 30% ,  对应的固化土 7 、14 、28 d 抗压强度分别达到 5. 11 、6. 16 、10. 71 MPa。进一步按粉煤灰与偏高岭土质量比 1 : 1 调整硅铝比， 7 d 强度较基准组提升 77. 9% ,  地聚物固化土在硫酸盐溶液中未出现膨胀开裂 ，表现出良好的耐蚀性。该配比体系兼顾力学性能与环境适应性 ，可为黄土地区低碳地基处理提供技术支持。

关键词：粉煤灰 ；地聚物 ；铝质校正料 ；耐久性

中图分类号：TU433            

文献标志码：A           

文章编号： 1005- 8249   (2025)  05- 0008- 06

DOI:10. 19860/j.cnki.issn1005 - 8249.2025 .05 .002

BAI Yanping¹  ,  XIA Yi ¹  ,  MA Lei ¹  ,  LUO Yiping²

( 1 . State Grid Gansu Linxia Power Supply Company ,  Linxia 731100 ,  China;  2. State  Key Laboratory of Eco - hydraulics  in Northwest Arid Region ,  Xi ’an University of Technology ,  Xi ’an 710048 ,  China)

 Abstract :  The purpose of this study is to develop fly ash based polymer curing agent to replace cement for loess reinforcement. The alkali activator was  prepared  by  using fly  ash  as  the  main  precursor ,  metakaolin  as  the  aluminum  correction  material , sodium silicate and sodium hydroxide . The  effects  of alkali activator modulus ,  solid content and fly ash content on compressive strength were investigated by orthogonal test. The results  show that the optimal ratio of alkali activator modulus is  1 . 1 , the solid content is 7% , and  the  fly  ash  content  is  30% . The  compressive  strength  of  the  corresponding  solidified  soil  at  7 days , 14 days ,  and 28  days  reaches  5. 11  MPa , 6. 16  MPa , and  10. 71 MPa , respectively. The silica - alumina  ratio  was  further adjusted according to the mass ratio of fly ash to metakaolin of 1 : 1 , and the 7 - day strength was 

77. 9%  higher than that of the reference group . The  geopolymer  solidified soil  did  not  expand  and  crack  in  the sulfate  solution , showing  good corrosion resistance . The  ratio  system  takes  into  account both  mechanical  properties  and  environmental  adaptability ,  and  can provide technical support for low - carbon foundation treatment in loess  areas .

Key words :  fly ash;  geopolymer;  aluminum correction material;  durability