( 1 .  华新水泥股份有限公司 ，黄石 435004 ;  2.  华新水泥技术管理（武汉） 有限公司 ，武汉 430073)

摘   要 ：针对超高性能混凝土  (UHPC)   在桥梁接缝工程应用中存在的早期强度低 、收缩大的问题 ，研究了硫铝酸盐水泥  (SAC) 、石膏 、酒石酸 、碳酸锂以及减缩剂对低收缩早强 UHPC 工作性能 、力学性能以及体积稳定性能的影响规律。结果表明 ，掺加 30%  SAC 和 6% 石膏的 UHPC 具有良好的力学性能和体积稳定性能 ，0. 3%的酒石酸和 0. 02% 碳酸锂可以改善早强 UHPC 工作性能与力学性能 ，1% 减缩剂可以明显降低早强 UHPC  自收缩 ，制备的低收缩早强超高性能混凝土 4 h 抗压强度大于 40 MPa 、28 d 抗压强度大于 120 MPa 、72 h  自收缩小于160 ×10 - 6 、28 d 干燥收缩小于 110 ×10 - 6 。研究结果可为相关应用提供参考。

关键词：低收缩 ；早强 ；超高性能混凝土 ；硫铝酸盐水泥 ；干燥收缩 ； 自收缩

中图分类号：TU528           

文献标志码：A            

文章编号： 1005- 8249   (2025)  05- 0014- 06

DOI:10. 19860/j.cnki.issn1005 - 8249.2025 .05 .003

 

LIU Yongqiang1 , 2

(  1 . Huaxin  Cement Co . ,  Ltd . ,  Huangshi 435004 ,  China;  2. Huaxin  Cement Technology Management  (  Wuhan)  Co . , Ltd . , Wuhan 430073 , China  )

Abstract :  Aiming at  the  problems  of  low  early  strength  and  large  shrinkage  in  the  application  of  ultra -  high  performance concrete  (UHPC)  in  bridge joint  engineering , the influence laws of sulphoaluminate cement  (SAC) , gypsum ,  tartaric acid , lithium carbonate and shrinkage reducing agent on the workability ,  mechanical properties and volume stability of low - shrinkage and early - strength  UHPC  were  studied .  The  results  show  that  UHPC  with  30% SAC  and  6% gypsum  has  good  mechanical properties and volume stability;  0. 3%  tartaric  acid  and 0. 02% lithium  carbonate  can  improve the workability and mechanical properties of early - strength UHPC ;  adding 1%  shrinkage reducing agent can significantly reduce the autogenous  shrinkage of early - strength UHPC . The  prepared  low - shrinkage  and  early - strength  ultra - high  performance  concrete  has  a  compressive strength of more than 40 MPa at 4 h , more  than  120  MPa  at  28  d , autogenous  shrinkage  less  than 160  ×10 - 6 at 72 h , and drying shrinkage less than 110 ×10 - 6  at 28  d . Research findings  can  provide references for related applications .

Key words :  low - shrinkage;  early - strength;  ultra - high performance  concrete; sulphoaluminate  cement;  drying shrinkage; self - shrinkage