PDF全文阅读

陆进保

 

（乌鲁木齐职业大学 应用工程学院 ，乌鲁木齐 830002)

摘 要 ：为分析纤维在粉煤灰加筋混凝土中 的 最 佳 应 用 方 案 ， 从 抗 压 强 度 性 能 角 度 开 展 其 研 究 。 以P ·O 42 . 5 普通硅酸盐水泥 ， Ⅰ级 FA 和不同长度的 PVA 纤维作为主要试验材料 ，构建了三因素四水平正交试验组 ，配合 GFRP 筋生成 100 mm ×100 mm ×100 mm 的试样。对不同配比组试件进行抗压性能测试 ，通过极差分析法优化参数组合。结果表明：PVA 纤维在 30 ~ 40 mm 长度区间时试件抗压性能达到峰值 ；当纤维体积掺量由0. 1% 增至 0. 3% 时 ，材料强度呈现显著协同效应。当 PVA 纤维为 30 ~ 40  mm 长度区间 、FA 掺量为 15. 0% 和PVA 纤维体积掺量为 0. 3% 时 ，可以在基体中形成有效三维乱向支撑体系 ，提升结构承载力 ，具有较优的抗压强度 ，为该材料在工程应用中的优化设计提供了关键依据。

关键词：纤维增强粉煤灰加筋混凝土 ；抗压强度 ；纤维长度 ；体积掺量

中图分类号：TU528 . 572           

文献标志码：A           

 文章编号： 1005- 8249   (2025)  05- 0020- 05

DOI:10. 19860/j.cnki.issn1005 - 8249.2025 .05 .004

 

LU Jinbao

(School of Applied Engineering ,  Urumqi Vocational University ,  Urumqi 830002 ,  China)

Abstract :  To  analyze  the  optimal  application  scheme  of  fibers  in  fiber - reinforced fly ash  reinforced  concrete , research  is conducted from the perspective of compressive strength performance . A three factor four level orthogonal  experimental group was constructed using P ·O 42. 5 ordinary Portland cement ,  grade I FA ,  and PVA fibers of different lengths as the main experimental materials. Samples  of  100  mm ×100  mm ×100  mm  were  generated  using  GFRP  reinforcement.  Using  the  WAW - 1000  electro - hydraulic servo  test  system , compressive  performance  tests  were  conducted on specimens with different ratios under  constant loading rate  conditions , and  parameter  combinations  were  optimized  through  range analysis .  The  results  showed  that  the compressive performance of PVA  fibers  reached  its  peak  in  the  length  range of 30 - 40mm; When  the  fiber  volume  fraction increases from 0. 1%  to 0. 3% , the  material  strength  exhibits  a significant synergistic  effect.  when  the  PVA fiber is  in the length range of 30 - 40mm ,  the  FA  content  is  15. 0% , and the  PVA fiber volume  content  is 0. 3% ,  an  effective  three - dimensional random support system  can be formed  in the  matrix ,  which  can  improve  the  structural  bearing  capacity  and  have better compressive strength . This  provides  a key basis for the optimization design of the material in engineering applications .

Key words :  fiber reinforced coal ash reinforced concrete;  compressive strength;  fiber length;  volume  incorporation  dosage