周昌文¹ ,  吴兴民² , 严   俊¹ ,  刘明亮¹ ,  魏    伟² ,  汪嫦红² ,  闫   革^2 ,3

 

( 1. 武汉博宏建设集团有限公司 , 武汉   430050 ;  2.  武汉市汉阳市政建设集团有限公司 ,  武汉   430050 ;

3. 武汉钟鑫建设集团有限公司 , 武汉   430050)

摘  要 :  为实现工程渣土就地再利用 ,  以武汉某工程基坑开挖黏土为原料土 , 采用水泥 、粉煤灰作为固化剂配置流态固化土 , 对流态固化土的流动性与无侧限抗压强度进行试验研究 , 研究不同水固比 、固化剂掺量对黏土制备流态固化土工作性能与力学性能的影响 , 并通过 SEM 电镜扫描分析其微观结构 。结果表明 :  固化土流动度值受水固比影响较大 , 受固化剂掺量影响较小 ;  固化土抗压强度随固化剂掺量增大大致呈线性增长趋势 ,水固比增大导致强度大幅下降 ; 水化反应过程中生成大量的 C-S-H 、AFt 是提高固化土强度的主要因素 ;  固化剂掺量 8% 、水固比≤0. 68 时 ,  流态固化土 28 d 强度 ≥0. 50 MPa , 微观结构致密 , 推荐使用该配合比作为施工最佳配合比 ; 本研究成果可为武汉地区黏土的资源化处理与工程应用提供理论依据和技术参数。

关键词 : 流态固化土 ; 配合比设计 ; 流动值 ; 抗压强度 ; 微观结构

中图分类号 : TU44          文献标志码 :  A           文章编号 :  1005- 8249  (2026)  03-0032-05

DOI :10. 19860/j. cnki. issn1005- 8249. 2026. 03. 006

 

ZHOU Changwen¹ , WU Xingmin² , YAN Jun¹ , LIU Mingliang¹ , WEI Wei² , WANG Changhong² , YAN Ge^{2 ,3} 

( 1. Wuhan Bohong Construction Group Co. ,  Ltd.  ,  Wuhan 430050 ,  China

2. Wuhan Hanyang Municipal Construction Group Co. ,  Ltd.  ,  Wuhan 430050 ,  China;

3. Wuhan Zhongxin Construction Group Co. ,  Ltd.  ,  Wuhan 430050 ,  China)

Abstract :  To achieve in-situ reuse of engineering sediment , fluidized solidified soil was prepared using excavated clay from a foundation pit in Wuhan as raw material , with cement and fly ash  as  solidfiers.   Experimental  studies  were  conducted  on  the fluidity and unconfined compressive  strength of the flowable  solidified  soil.   The  effects  of  different  water - to - solid ratios  and solidifier  contents  on  the  workability  and  mechanical  properties  of  the  flowable   solidified  soil  prepared  from  clay  were investigated , and its microstructure was analyzed by SEM scanning.   The  results  show  that the fluidity of the  solidified soil is significantly influenced by the water-to - solid ratio but less affected by the solidifier content.   The  compressive  strength of the solidified soil increases approximately linearly with the increase of solidifier content , while a higher water-to-solid ratio leads to a significant decrease in strength.   When the solidifier content is 8% and the water-to-solid ratio is  ≤0. 68 , the 28-day strength of the flowable solidified soil reaches  ≥0. 50 MPa , and the microstructure is very dense ,  which is recommended as the optimal mix proportion for construction.   The research provides theoretical basis and technical parameters for the resource utilization and engineering application of clay in the Wuhan region.

Key words :  fluidized solidified soil; mix ratio; flow value ; compressive strength; microstructure