尹   健

 

( 北京城建房地产开发有限公司 , 北京   100010 )

摘  要 :  采用 5% 、10%和 15%的粉煤灰等量替代水泥配制混凝土 ,  通过抗压强度 、抗折强度 、劈裂抗拉强度试验以及硫酸侵蚀 、吸水率和孔隙率测试 , 研究不同替代率下混凝土的力学性能及抗硫酸侵蚀性能 。结果表明 : 粉煤灰替代率为 10%时 , 混凝土养护 28 d 后的抗压强度 、抗折强度及劈裂抗拉强度均达到最优 ;  当替代率增至 15%时 , 各项强度明显下降 。硫酸侵蚀作用下 ,  混凝土抗压强度损失率和质量损失率均随粉煤灰替代率增加而增大 , 高替代率条件下劣化更为明显 。与此同时 , 混凝土吸水率和孔隙率随粉煤灰替代率增加而增加 , 表明其内部结构在酸性环境中更易受损 。综合来看 , 适量粉煤灰可改善混凝土力学性能 , 但过高替代率不利于其抗硫酸侵蚀性能 , 研究成果可为粉煤灰混凝土的工程应用提供试验依据。

关键词 : 粉煤灰 ; 混凝土 ; 耐久性 ; 抗压强度损失 ; 孔隙率

中图分类号 : TU528           文献标志码 : A           文章编号 :  1005- 8249  (2026)  03-0079-05

DOI :10. 19860/j. cnki. issn1005- 8249. 2026. 03. 013

 

YIN Jian

( Beijing Urban Construction Real Estate Development Co. , Ltd. ,  Beijing 100010 , China)

Abstract :  Concrete was prepared by  replacing  cement  with 5% ,  10% ,  and  15%  fly  ash  in  equal  amounts.   The  mechanical properties and sulfuric acid resistance  of the  concrete  under  different  replacement  rates were  investigated  through  compressive strength , flexural strength , splitting tensile strength tests , sulfuric acid attack tests , water absorption tests , and porosity tests. The results showed that when the fly ash replacement rate was  10% , the compressive strength , flexural strength , and splitting tensile strength of the  concrete  reached their  optimal values  after 28  days  of curing.   When  the  replacement  rate  increased  to 15% , all strengths decreased significantly.  Under sulfuric acid attack , the loss rate of compressive strength and the loss rate of mass of the concrete increased with the increase of the fly ash replacement rate , with more significant deterioration under high replacement rate conditions.  Simultaneously , the water absorption and porosity of the concrete increased with the increase of the fly ash  replacement  rate ,  indicating  that its internal structure is more susceptible to damage in an acidic environment.  In summary , an  appropriate  amount  of  fly  ash  can  improve  the  mechanical  properties  of  concrete ,   but  an  excessively  high replacement rate  is  detrimental  to  its  sulfuric  acid  attack  resistance.   This   study   provides  experimental  evidence  for  the engineering application of fly ash concrete.

Key words :  fly ash; concrete ; durability; compressive strength loss ; porosity